TY - JOUR
T1 - Epitaxial growth of (Na,K)NbO3 based materials on SrTiO3 by pulsed laser deposition
AU - Hanawa, T.
AU - Kikuchi, N.
AU - Nishio, K.
AU - Tonooka, K.
AU - Wang, R.
AU - Mamiya, T.
N1 - Publisher Copyright:
© 2014 Materials Research Society.
PY - 2014/11/7
Y1 - 2014/11/7
N2 - Lead-free, piezoelectric (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films were epitaxially grown onto (100) SrTiO3 substrate via pulsed laser deposition. The effects of post-annealing temperature on the crystal phases, mosaic spread, and chemical composition of the deposited (Na,K)NbO3 and (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films were analyzed. Results indicate the epitaxial growth of (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films deposited at an oxygen pressure (PO2) of ≥40 Pa and substrate temperature (Ts) of 800°C. The alkaline-deficiency could be suppressed in the (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films deposited at PO2 ≥ 70 Pa. AFM profile of the (Na,K)NbO3 post-annealed at 1000°C indicates the epitaxial growth of film with atomically flat step-terrace structure, while that of the (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 film post-annealed at 1200°C shows relatively smooth surface with step-terrace structure and several cubic crystals. It was also found that the preferential evaporation of alkaline components could be suppressed by annealing under covered substrate condition.
AB - Lead-free, piezoelectric (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films were epitaxially grown onto (100) SrTiO3 substrate via pulsed laser deposition. The effects of post-annealing temperature on the crystal phases, mosaic spread, and chemical composition of the deposited (Na,K)NbO3 and (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films were analyzed. Results indicate the epitaxial growth of (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films deposited at an oxygen pressure (PO2) of ≥40 Pa and substrate temperature (Ts) of 800°C. The alkaline-deficiency could be suppressed in the (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films deposited at PO2 ≥ 70 Pa. AFM profile of the (Na,K)NbO3 post-annealed at 1000°C indicates the epitaxial growth of film with atomically flat step-terrace structure, while that of the (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 film post-annealed at 1200°C shows relatively smooth surface with step-terrace structure and several cubic crystals. It was also found that the preferential evaporation of alkaline components could be suppressed by annealing under covered substrate condition.
KW - epitaxy
KW - laser ablation
KW - piezoelectric
UR - http://www.scopus.com/inward/record.url?scp=84910148788&partnerID=8YFLogxK
U2 - 10.1557/opl.2014.84
DO - 10.1557/opl.2014.84
M3 - Article
AN - SCOPUS:84910148788
VL - 1633
SP - 19
EP - 24
JO - Journal of British Studies
JF - Journal of British Studies
SN - 0021-9371
IS - 3
ER -