Densification of Y2O3 by flash sintering under an AC electric field

Kohta Nambu, Koji Morita, Kohei Soga, Takahisa Yamamoto, Hiroshi Masuda, Hidehiro Yoshida

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Frequency dependence of the densification behavior of undoped Y2O3 sintered by the AC-flash sintering was systematically investigated at 500 V·cm−1 over a frequency range from 0.05 Hz to 1 kHz. The Y2O3 bodies sintered under an AC field showed a uniform microstructure, without an asymmetric grain size distribution between the electrodes. Almost fully-densified Y2O3 body was consolidated at 1 kHz exhibited a relative density greater than 99 % and an average grain size of 1.6 μm. The almost full densification probably resulted from the high input power at the relatively high onset temperature of 1300 °C at this frequency. The temperature dependence of the power dissipation during the AC-flash sintering experiments can be ascribed to the periodic fluctuations of the specimen temperature at low frequencies and to the phase shift between the applied field and the specimen current at high frequencies.

本文言語English
ページ(範囲)567-575
ページ数9
ジャーナルJournal of the European Ceramic Society
42
2
DOI
出版ステータスPublished - 2月 2022

フィンガープリント

「Densification of Y2O3 by flash sintering under an AC electric field」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル